DSC and TMDSC study of melting behaviour of poly(butylene succinate) and poly(ethylene succinate) |
| |
Authors: | Zhaobin Qiu Motonori KomuraTakayuki Ikehara Toshio Nishi |
| |
Affiliation: | a Department of Organic and Polymeric Materials, Graduate School of Science and Engineering, Tokyo Institute of Technology, 2-12-1 Ohokayama, Meguro-ku, Tokyo 152-8552, Japan b Department of Applied Physics, School of Engineering, The University of Tokyo, 7-3-1, Hongo, Bunkyo-ku, Tokyo 113-8656, Japan c Department of Applied Chemistry, Faculty of Engineering, Kanagawa University, 3-27-1, Rokkakubashi, Kanagawa-ku, Yokohama 221-8686, Japan |
| |
Abstract: | The subsequent melting behaviour of poly(butylene succinate) (PBSU) and poly(ethylene succinate) (PES) was investigated using DSC and temperature modulated DSC (TMDSC) after they finished nonisothermal crystallization from the melt. PBSU exhibited two melting endotherms in the DSC traces upon heating to the melt, which was ascribed to the melting and recrystallization mechanism. However, one melting endotherm with one shoulder and one crystallization exotherm just prior to the melting endotherm were found for PES. The crystallization exotherm was ascribed to the recrystallization of the melt of the crystallites with low thermal stability, and the shoulder was considered to be the melting endotherm of the crystallites with high thermal stability. The final melting endotherm was ascribed to the melting of the crystallites formed through the reorganization of the crystallites with high thermal stability during the DSC heating process. TMDSC experiments gave the direct evidences to support the proposed models to explain the melting behaviour of PBSU and PES crystallized nonisothermally from the melt. |
| |
Keywords: | Poly(butylene succinate) Poly(ethylene succinate) Melting behaviour |
本文献已被 ScienceDirect 等数据库收录! |
|