| T1O钢冲模开裂原因分析 |
| |
| 引用本文： | 张宇巍. T1O钢冲模开裂原因分析[J]. 热处理技术与装备, 2011, 32(4): 50-51 |
| |
| 作者姓名： | 张宇巍 |
| |
| 作者单位： | 哈尔滨理工大学,黑龙江哈尔滨,150080 |
| |
| 摘 要： | 分析T10钢冲模裂纹形态、化学成分、低倍和高倍金相组织,找出开裂原因,提出改进措施.
|
| 关 键 词： | 冲模裂纹 原因分析 改进措施 |
Analysis Cracking Reason T10 Steel Dies |
| |
| ZHANG Yu-wei. Analysis Cracking Reason T10 Steel Dies[J]. Heat Treatment Technology and Equipment, 2011, 32(4): 50-51 |
| |
| Authors: | ZHANG Yu-wei |
| |
| Affiliation: | ZHANG Yu-wei (Harbin Institute of Technology University of Heilongjiang,Harbin Heilongjiang 150080,China) |
| |
| Abstract: | Analyzing the cracking form of T10 steel dies,chemical composition,low and high magnification microstructure,the cracking reasons are found and the improvement measures are put forward. |
| |
| Keywords: | die crack Cause analysis improvement measures |