Ni-W-ZrO2复合镀层的制备及耐腐蚀性能
引用本文:舒霞,李云,吴玉程,黄新民,郑玉春. Ni-W-ZrO2复合镀层的制备及耐腐蚀性能[J]. 复合材料学报, 2007, 24(6): 116-120
作者姓名:舒霞  李云  吴玉程  黄新民  郑玉春
作者单位:合肥工业大学 材料科学与工程学院, 合肥 230009
基金项目:安徽省科委重点项目(05022047)
摘    要:采用电沉积方法制备Ni-W-ZrO2复合镀层, 研究了微粒的分散特性及镀液中微粒含量、 电流密度、 pH值、 温度等因素对Ni-W-ZrO2镀层沉积速率、 显微硬度、 镀层外观的综合影响, 优化得到Ni-W-ZrO2复合镀层的电沉积工艺为: Ni-W基础镀液中ZrO2添加量为10g/L, pH=7, 镀液温度为60~70℃, 电流密度为15A/dm2, 所获得的镀层硬度>HV800(×9.8MPa)。通过电化学技术研究了复合镀层在3.0wt%NaCl溶液中的耐腐蚀性能, 结果表明, Ni-W-ZrO2复合镀层有明显的钝化区间。 

关 键 词:电沉积   Ni-W-ZrO2   复合镀层   耐腐蚀性能
文章编号:1000-3851(2007)06-0116-05
收稿时间:2006-12-25
修稿时间:2007-05-08

Preparation and corrosion resistance of Ni-W-ZrO2 composite coatings by electrodeposition
SHU Xia,LI Yun,WU Yucheng,HUANG Xinmin,ZHENG Yuchun. Preparation and corrosion resistance of Ni-W-ZrO2 composite coatings by electrodeposition[J]. Acta Materiae Compositae Sinica, 2007, 24(6): 116-120
Authors:SHU Xia  LI Yun  WU Yucheng  HUANG Xinmin  ZHENG Yuchun
Affiliation:School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China
Abstract:The Ni-W-ZrO2 composite coatings were prepared by electrodeposition. The dispersible characteristics of particles were studied. The effects of the main factors, such as adding particle quantity, current density, pH value and temperature on the hardness, deposition rate and surface of Ni-W-ZrO2 composite coatings were investigated. The process parameters of Ni-W-ZrO2 composite coatings were obtained through optimization: the adding particle quantity is 10 g/L, current density is 15 A/dm2, pH value is 7 and temperature is 60~70 ℃. The microhardness of Ni-W-ZrO2 coatings reaches higher than HV800(×9.8MPa). The corrosion resistance was studied by the electrochemical techniques, and the results show that the Ni-W-ZrO2 composite coatings have obvious passivation.
Keywords:electrodeposition   Ni-W-ZrO2    composite coating   corrosion resistance