| 环氧灌注料开裂问题及采取的措施 |
| |
| 引用本文： | 黄文虎.环氧灌注料开裂问题及采取的措施[J].粘接,2002,23(6):51-52. |
| |
| 作者姓名： | 黄文虎 |
| |
| 作者单位： | 武汉七一零厂,武汉市,430015 |
| |
| 摘 要： | 从断裂力学的角度分析了环氧树脂灌注料在灌封电子变压器时产生裂纹的原因，针对灌注料中存在的内应力及其他缺陷提出了预防和解决的具体措施。
|
| 关 键 词： | 环氧灌注料 开裂 措施 灌封 应力 电子变压器 |
| 文章编号： | 1001-5922(2002)06-0051-02 |
| 修稿时间： | 2002年9月10日 |
Fracture initiation in epoxy resin pouring sealent and preventive measures |
| |
| Huang Wenhu.Fracture initiation in epoxy resin pouring sealent and preventive measures[J].Adhesion in China,2002,23(6):51-52. |
| |
| Authors: | Huang Wenhu |
| |
| Abstract: | From the viewpoint of fracture mechanics,the reasons to produce the cracks during pouring of the epoxy pouring sealent and sealing of the electronic transformer were analysed.To counler the existence of internal stress and other defects the preventive measures and some concrete solutions were presented. |
| |
| Keywords: | Epoxy resin Pouring sealent Stress crack |