Lanthanum-Magnesium and Lanthanum-Manganese Donor-Acceptor-Codoped Semiconducting Barium Titanate

BaTiO₃ powder doped with La donor and codoped with Mn or Mg acceptor was sintered at 1350°C/1 h in air. For Ladoped BaTiO₃, the room-temperature resistivity decreased to a minimum at La³⁺] ～ 0.15 mol%. For La-Mn-codoped BaTiO₃, the minimum resistivity occurred at La³⁺] - 2Mn²⁺] ～ 0.15 mol%. When the ceramic was changed to a fine-grained insulator by high donor doping (La³⁺] >0.15 mol%), its semiconductivity was restored, and the relatively homogeneous, coarse-grained microstructure recurred by codoping with either Mg or Mn acceptor, with the transition at La³⁺] - 2Mg²⁺] = 0.15 mol% or La³⁺] - 2Mn²⁺] = 0.15 mol%. The analogy of a compensation effect between La-Mn- and La-Mg-codoped BaTiO₃ suggested that Mn acceptor added to BaTiO₃ exists as Mn²⁺ ion in the bulk grain region; its influence on the positive temperature coefficient of resistivity behavior is then discussed.