阻燃涤纶工业丝的制备及性能研究

对普通阻燃聚酯切片进行干燥增黏,得到低含水率的高黏度聚酯阻燃切片,再通过优化纺丝工艺,生产制备得到阻燃涤纶工业丝。利用差示扫描量热仪、热重分析仪、极限氧指数仪和纤维强伸仪等对样品的熔点、热焓、阻燃性、热稳定性和力学性能进行分析测试,结果表明:干燥增黏的切片在挤出温度284~305℃、拉伸定形温度90~230℃、卷绕速度2 700~2 900 m/min的工艺条件下纺丝,得到质量稳定的阻燃涤纶工业丝,其断裂强度为6.52 c N/dtex,断裂伸长率为17.1%,极限氧指数为31.5%。该产品的断裂强度高、断裂伸长率低、力学性能稳定并具备优良的阻燃特性。

Preparation and Research of Flame Retardant Industrial Polyester Fiber

The normal flame retardant polyester chips were employed to prepare the high viscosity polyesterchips,then the polyester industrial fibers were obtained through the optimized technological parameters.The melting point,enthalpy,flame retardancy,thermal stability and mechanical properties were analyzed bydifferential scanning calorimetry,thermogravimetric analyzer,limit oxygen index and fiber strength measure-ment.The results showed that the stable quality industrial flame retardant polyester fibers were producedwhen the extrusion temperature 284~305 ℃,drawing and setting temperature 90~230 ℃,winding speed2 700~2 900 m/min,after tackifying technology(the moisture content was 0.001 7%) and melt spinning un-der the optimized parameters.The products owned a satisfied mechanical properties and excellent flame re-tardancy(LOI up to 31.5%).