| 有机涂层耐阴极剥离的影响因素研究进展 |
| |
| 引用本文： | 姚竟迪,梁成浩,黄乃宝,吴建华.有机涂层耐阴极剥离的影响因素研究进展[J].表面技术,2014,43(3):137-143,151. |
| |
| 作者姓名： | 姚竟迪 梁成浩 黄乃宝 吴建华 |
| |
| 作者单位： | 大连海事大学 交通运输装备与海洋工程学院, 辽宁 大连 116026;大连海事大学 交通运输装备与海洋工程学院, 辽宁 大连 116026;大连海事大学 交通运输装备与海洋工程学院, 辽宁 大连 116026;中船重工七二五研究所 海洋腐蚀与防护国防科技重点实验室, 福建 厦门 361101 |
| |
| 基金项目： | 国家自然科学基金(21276036) ;中央高校基本科研业务费专项资金资助(3132014323) |
| |
| 摘 要： | 有机涂层在服役期间,阴极剥离是使其失效的主要形式之一。综述了国内外海水、淡水、土壤环境中,有机涂层耐阴极剥离影响因素的研究进展。介绍了有机涂层阴极剥离过程,阐述了影响涂层耐阴极剥离的因素——树脂、颜填料、助剂以及表面处理、涂层厚度和缺陷等,并指出了耐阴极剥离有机涂层主要研究方向的发展趋势。
|
| 关 键 词： | 有机涂层 金属防护 阴极剥离 影响因素 |
| 收稿时间： | 1/6/2014 12:00:00 AM |
| 修稿时间： | 2014/2/12 0:00:00 |
Research Progress in Influencing Factors of Cathodic Disbondment of Organic Coatings |
| |
| YAO Jing-di,LIANG Cheng-hao,HUANG Nai-bao and WU Jian-hua.Research Progress in Influencing Factors of Cathodic Disbondment of Organic Coatings[J].Surface Technology,2014,43(3):137-143,151. |
| |
| Authors: | YAO Jing-di LIANG Cheng-hao HUANG Nai-bao and WU Jian-hua |
| |
| Affiliation: | Transportation Equipments & Ocean Engineering College, Dalian Maritime University, Dalian 116026, China;Transportation Equipments & Ocean Engineering College, Dalian Maritime University, Dalian 116026, China;Transportation Equipments & Ocean Engineering College, Dalian Maritime University, Dalian 116026, China;State Key Laboratory for Marine Corrosion and Protection, China Shipbuilding Industry 725 research institute, Xiamen 361101, China |
| |
| Abstract: | Cathodic disbonding is one of the main forms of organic coating failure during service. The research progress in the influencing factors of resistance against cathodic disbonding of organic coatings in the seawater, fresh water and soil were summarized. The cathodic disbonding process of organic coating and the influencing factors of coating resistance against cathodic disbonding including resins, pigments and fillers, additives and surface treatment, coating thickness and defect were introduced. The questions remaining to be resolved in future were presented and the trend of future development was discussed. |
| |
| Keywords: | organic coating metal protection cathodic disbanding influencing factors |