The diffusion and solubility of oxygen in solid nickel

Solid-state electrochemical measurements using various experimental procedures were made with the double cell: $$ Ni + NiO|ZrO_2 + Y_2 O_3 |Ni + \underline O |ZrO_2 + Y_2 O_3 |Ni + NiO $$ to determine the diffusivity and thermodynamic functions of oxygen dissolved in solid nickel. Non-steady state diffusion of oxygen in the specimen was caused by applying a preselected potential between the reference and specimen electrodes and was monitored by measuring time-dependent potentials and/or currents. The following results were obtained for the diffusivity of oxygen and the solubility of oxygen in nickel in equilibrium with NiO: $$D{\text{ = 4}}{\text{.9 }} \times {\text{ 10}}^{{\text{ - 2}}} {\text{ exp}}\left( {{\text{ - }}\frac{{{\text{164 kJ/mole}}}}{{{\text{R}}T}}} \right){\text{cm}}^{\text{2}} /{\text{sec (850 to 1400 }}{}^{\text{o}}{\text{C)}}$$ $$C_{\text{O}}^s {\text{ = 8}}{\text{.3 exp}}\left( { - \frac{{55{\text{kJ/mole}}}}{{{\text{R}}T}}} \right){\text{at}}{\text{. pct (800 to 1000 }}{}^{\text{o}}{\text{C)}}$$ The thermodynamic and transport behaviors of oxygen in solid nickel were fairly well described by a simple quasi-regular model and an interstitial diffusion model, respectively.