Reinvestigation of Al–Si Spinel Phase in Diphasic Al2O3–SiO2 Gel

Mechanical mixture of γ-Al₂O₃ and amorphous SiO₂, and diphasic Al₂O₃/SiO₂ gels of three different compositions were synthesized. They were subjected to heat treatment to various temperatures in the range 900°–1600°C. Qualitative X-ray diffraction data show that these diphasic gels do not crystallize to a combined mixture of θ-Al₂O₃ and α-Al₂O₃ polymorphs at the intermediate stage, prior to mullite formation. Estimated mullite formation data show that the course of its formation from mixed oxides was different from that of diphasic gels. Results are compared with previous findings and the concept of Al–Si spinel formation in the phase transformation of stoichiometric diphasic gel system is substantiated.