Effects of Al2O3 Particulates on the Thickness of Reaction Layer of Al2O3 Joints Brazed with Al2O3-Particulate-Contained Composite Filler Materials

In order to understand the rate-controlling process for the interracial layer growth of brazing joints brazed with active composite filler materials, the thickness of brazing joints brazed with conventional active filler metal and active composite filler materials with different volume fraction of AI203 particulate was studied. The experimental results indicate although there are Al2O3 particulates added into active filler metals, the time dependence of interracial layer growth is t^2 as described by Fickian law for the joints brazed with conventional active filler metal. It also shows that the key factor affecting the interracial layer growth is the volume fraction of alumina in the composite filler material compared with the titanium weight fraction in the filler material.

Effects of Al2O3 Particulates on the Thickness of Reaction Layer of Al2O3 Joints Brazed with Al2O3-Particulate-Contained Composite Filler Materials

In order to understand the rate-controlling process for the interfacial layer growth of brazing joints brazed with active composite filler materials, the thickness of brazing joints brazed with conventional active filler metal and active composite filler materials with different volume fraction of AI2O3 participate was studied. The experimental results indicate although there are Al2O3 particulates added into active filler metals, the time dependence of interfacial layer growth is t2 as described by Fickian law for the joints brazed with conventional active filler metal. It also shows that the key factor affecting the interfacial layer growth is the volume fraction of alumina in the composite filler material compared with the titanium weight fraction in the filler material.