Influence of DMF on the polymerization of tert‐butyl acrylate initiated by 4‐oxo‐TEMPO‐capped polystyrene macroinitiator

BACKGROUND: In a number of studies it has been shown that 2,2,6,6‐tetramethylpiperidinooxy (TEMPO)‐mediated polymerization of acrylates is not facile. Therefore, the object of the study reported here was to prepare polystyrene‐block‐(tert‐butyl acrylate)] (PS‐b‐PtBA) block copolymers using 4‐oxo‐TEMPO‐capped polystyrene macroinitiator as an initiator, in the presence of small amounts of N,N‐dimethylformamide (DMF). The kinetic analysis and the effect of DMF on the reaction mechanism are also discussed. RESULTS: PS‐b‐PtBA block copolymer was prepared through polymerization of tert‐butyl acrylate (tBA) initiated by 4‐oxo‐TEMPO‐capped polystyrene macroinitiator at 135 °C. The polymerization rate of tBA could be increased by adding a small amount of DMF, and the number average molecular weight of the PtBA block in PS‐b‐PtBA reached 10 000 g mol^?1 with narrow polydispersity. The activation rate constant k_act?tBA of alkoxyamine increased and the recombination rate constant k_rec?tBA decreased with increasing DMF concentration. CONCLUSION: DMF was shown to be a rate‐enhancing additive for the polymerization of tBA using a 4‐oxo‐TEMPO‐capped polystyrene macroinitiator. From the kinetic analysis, it was concluded that the improvement of polymerization with the addition of DMF was due to an increase in k_act?tBA and a decrease in k_rec?tBA. Copyright © 2008 Society of Chemical Industry