Effects of microstructure on flexural strength of biomorphic C/SiC composites |
| |
Authors: | Hee S. Park Jong J. Jang Kyong H. Lee Kwang H. Lim Sang B. Park Yun C. Kim Soon H. Hong |
| |
Affiliation: | (1) Department of Materials Science and Engineering, KAIST, Yuseong-Gu, Daejeon, 307-701, Korea;(2) Daeyang Ind., Co., Icheon-city, Gyeonggi-do, 467-813, Korea;(3) Korea Forest Research Institute, Dongdaemun-gu, Seoul, 130-712, Korea;(4) Agency for Defense Development, Yuseong-gu, Daejeon, 305-152, Korea |
| |
Abstract: | Biomorphic C/SiC composites were fabricated from different kinds of wood by liquid silicon infiltration (LSI) following a two-step process. In the first-step, the wood is converted into carbon preforms by pyrolysis in a nitrogen atmosphere. The carbon preforms are then infiltrated by silicon melt at 1,560°C under vacuum to fabricate C/SiC composites. The mechanical properties of the C/SiC composites were characterized by flexural tests at ambient temperature, 1,000, and 1,300°C, and the relationship between mechanical properties and microstructure was analyzed. The flexural strength of the biomorphic composites was strongly dependent on the properties of the carbon preforms and the degree of silicon infiltration. The flexural strength increased with increasing SiC content and bulk density of composite, and with decreasing porosity in the C/SiC composite. An analysis of fractographs of fractured C/SiC composites showed a cleavage type fracture, indicating brittle fracture behavior. |
| |
Keywords: | Biomorphic C/SiC Composites Liquid silicon infiltration Carbon preform Flexural strength |
本文献已被 SpringerLink 等数据库收录! |
|