Vaporization of LaCrO3: Partial and Integral Thermodynamic Properties

The vaporization of LaCrO₃(s) and samples of the composition LaCrO₃+ La₂O₃ was investigated in the temperature range of 1887-2333 K by Knudsen effusion mass spectrometry using Knudsen cells made of tungsten lined completely with iridium. The species Cr(g), CrO(g ), CrO₂(g), and LaO(g) were identified in the vapor. Their partial pressures were determined by calibration with pure platinum solid. The thermodynamic activity of Cr₂O₃, a _cr2o₃ in LaCrO₃ for the Cr₂0₃-poor phase boundary of this phase was In a_Cr2o₃⁼ -(17953/T) - 0.485 (temperature T given in K) for the temperature range of the measurements with a probable overall error of ± 13%. The following values and temperature dependence of ΔG°_f,T resulted for the formation of LaCrO₃(s) according to the reaction 0.5Cr₂O₃(s) + 0.5La₂O₃(s) → LaCrO₃(s): ΔG°_f,2100= -78.9 ± 1.1 kj/mol, Δ H°_f,298= -76.8 ± 5.2 kj/mol, and ΔG°_r(kJ/mol) = -74.7 - 0.00202 T . Computations for the vaporization of LaCrO₃ were conducted to show the volatility of this material in different atmospheres at high temperatures.