| 840D车轮辐板孔疲劳失效及裂纹容限研究 |
| |
| 引用本文： | 习年生,刘敬辉.840D车轮辐板孔疲劳失效及裂纹容限研究[J].失效分析与预防,2006,1(1):48-52. |
| |
| 作者姓名： | 习年生 刘敬辉 |
| |
| 作者单位： | 铁道科学研究院,铁道科学技术研究发展中心,北京,100081;铁道科学研究院,铁道科学技术研究发展中心,北京,100081 |
| |
| 摘 要： | 通过裂纹和断口的观察、理化检验、模拟仿真及其力学计算,分析了840D车轮辐板孔裂纹的特征、机理和原因.结果表明:裂纹属于高低周复合机械疲劳,裂纹主要在制动加机械载荷工况下萌生和扩展.统计分析确定了裂纹扩展速率,结合裂纹发展形态和理论计算给出了临界裂纹长度,进而评估出裂纹容限为20mm.
|
| 关 键 词： | 车轮 疲劳失效 裂纹容限 |
| 收稿时间： | 2005-09-06 |
| 修稿时间： | 2005-09-062005-10-08 |
Fatigue Failure and Crack Tolerance of 840D Wheel Web Hole |
| |
| XI Nian-sheng,LIU Jing-hui.Fatigue Failure and Crack Tolerance of 840D Wheel Web Hole[J].Failure Analysis and Prevention,2006,1(1):48-52. |
| |
| Authors: | XI Nian-sheng LIU Jing-hui |
| |
| Abstract: | Observation on cracks and fracture surfaces, physical testing, chemical analysis, computer simulation and mechanical calculation have been performed to analyze the characteristics, mechanism and causes of the cracks on 840D wheel web hole. Results show that, the cracking is a high- low cycle fatigue failure mainly under brake and mechanical loads. Crack growth rate is derived by statistical analysis, and critic crack length is determined based on configuration of crack propagation and theoretical calculation, then crack tolerance is evaluated as 20mm. |
| |
| Keywords: | wheel fatigue failure crack tolerance |