Influence of Sr on microstructure and mechanical properties of ZL114 cast alloy |
| |
Authors: | Dong Xugang Zhou Jie Jia Yaojun Liu Bin Lei Zhenzhen Wang Wenhao Bi Huan |
| |
Affiliation: | 1. College of Materials Science and Engineering, Chongqing University, Chongqing 400030, China 2. Baoji Petroleum Steel Pipe Co.,Ltd., Baoji 721008, China 3. College of Mechanical and Power Engineering, Chongqing University of Science & Technology, Chongqing 401331, China |
| |
Abstract: | In the present work,the effects of trace element Sr on the microstructure,tensile properties,fractography and morphology of the eutectic Si of ZL114A (Al-7Si) cast alloy were investigated.The cast ZL114A aluminum alloy was prepared using a metal mold,and then heat treated with the T6 technique.The test results of mechanical properties show that modification element Sr can improve significantly the ultimate tensile strength,elongation and hardness of the ZL114A-T6 aluminum alloy.By adding 0.04%Sr,the values of the tensile strength Rm,elongation A and hardness HB increase from 230 MPa,1% and 65 to the maximum of 305 MPa,8%,and 100,respectively.SEM analysis indicates that the near tensile fracture surface on longitudinal section of the ZL114A-T6 alloy reveals a transgranular fracture mode without Sr modification,while the tensile fracture is an intergranular fracture mode after Sr modification.The morphology of the eutectic Si phase is changed from acicular to fine fibrous. |
| |
Keywords: | aluminum alloy modification tensile properties fracture mechanism |
本文献已被 CNKI 万方数据 等数据库收录! |
|