Filament-assisted pulsed laser deposition of epitaxial PbZrxTi1?xO3 films: Morphological and electrical characterization

Abstract

A modification of the conventional pulsed laser deposition technique was employed, whereby a low energy electron emitting filament was placed between the target and the substrate (-20 V filament/substrate bias) in order to produce reactive species (O_2- and O_?) during deposition. Using this modification, epitaxial thin films of PbZr_xTi_1?xO3 (PZT, 0 ≤ × ≤ 0.6) were prepared in situ on virgin (100) MgO and (100) Pt/(100) MgO substrates at a substrate temperature of 550°C and in an oxygen ambient (0.3 Torr). The topography of films prepared without a filament on virgin MgO were porous and composed of grains of about 1000 Å in diameter. As the emission current was increased from 0 to 400 μA, the grain size decreased to less than 100 Å with a concomitant decrease in the porosity. The nucleation of crystallites of other orientations was observed at emission currents greater than about 500 μA. Trilayer structures (Pt/PZT/Pt/<100>MgO) were fabricated for electrical measurements. Non-filament-assisted PZT cells usually failed because of a high probability of conductive paths through the PZT layer. Filament-assisted films were much less prone to this problem. Typical remanent polarizations and coercive fields were 15–20 μC/cm² and 30–50 kV/cm, respectively.