Performance Enhancement of Tunable Bandpass Filters Using Selective Etched Ferroelectric Thin Films |
| |
Authors: | Felix A Miranda Carl H Mueller Fred W Van Keuls Guru Subramanyam Sivaruban Vignesparamoorthy |
| |
Affiliation: | 1. Glenn Research Center , NASA , 21000 Brookpark Road, Cleveland , Ohio , 54135;2. Analex Corporation , Cleveland , Ohio , 44135;3. The Ohio Aerospace Institute , Cleveland , Ohio , 44142;4. Department of Electrical and Computer Engineering , The University of Dayton , Dayton , Ohio , 45458 |
| |
Abstract: | The inclusion of voltage-tunable barium strontium titanate (BSTO) thin films into planar band pass filters offers tremendous potential to increase their versatility. The ability to tune the passband so as to correct for minor deviations in manufacturing tolerances, or to completely reconfigure the operating frequencies of a microwave communication system, are highly sought-after goals. However, use of ferroelectric films in these devices results in higher dielectric losses, which in turn increase the insertion loss and decrease the quality factors of the filters. This study explores the use of patterned ferroelectric layers to minimize dielectric losses without degrading tunability. Patterning the ferroelectric layers enables us to constrict the width of the ferroelectric layers between the coupled microstrip lines, and minimize losses due to ferroelectric layers. Coupled one-pole microstrip bandpass filters with fundamental resonaces at ~7.2 GHz and well-defined harmonic resonances at ~14.4 and ~21.6 GHz, were designed, simulated and tested. For one of the filters, experimental results verified that its center frequency was tunable by 528 MHz at a center frequency of 21.957 GHz, with insertion losses varying from 4.3 to 2.5 dB, at 0 and 3.5 V/ w m, respectively. These data demonstrate that the tuning-to-loss figure of merit of tunable microstrip filters can be greatly improved using patterned ferroelectric thin films as the tuning element, and tuning can be controlled by engineering the ferroelectric constriction in the coupled sections. |
| |
Keywords: | Bsto Tunable Filters Selective Etching Insertion Loss |
|
|