Device effects of various Zr/Ti ratios of PZT thin-films prepared by sol-gel method
Authors:H. Watanabe  T. Mihara  C. A. Paz De Araujo
Affiliation:1. Olympus Optical Co Ltd., Hachioji , Tokyo, 192, Japan;2. Microelectronics Research Laboratiries , University of Colorado , Colorado Springs
Abstract:Abstract

PZT, PbZrxTI1?xO3, thin-films with various Zr/Ti ratios, 100/0 (lead zirconate) to 0/100 (lead titanate), were prepared by the sol-gel method. Basic electric properties, dielectric constant, tan σ, P-E hysteresis curve, switching properties were measured respectively as a function of composition. Dielectric constant indicated a specific peak value (~1100) around the morphotropic phase boundary between tetragonal and rhombohedral phase. Satisfactory low-voltage saturated hysteresis curves were observed for the compositions of PZT(90/10) through PZT(20/80). The remanent polarization and the coercive field increased as the titanium content decreased. The result of X-ray measurement showed that the lattice constants of thin-Film PZT are different from bulk ceramics for compatible compositionsS. The boundary, on which the c/a ratio must be 1 (rhombohedral phase), was slightly shifted to PbTiO3 side. This distortion in crystal structure is considered to be due to the thin-film effect, which the lattice mismatch between the platinum substrate and the PZT layer, restricted the ions to position into proper cites.
Keywords:
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号