| 不锈钢管道的应力腐蚀开裂及对策 |
| |
| 引用本文： | 刘建忠. 不锈钢管道的应力腐蚀开裂及对策[J]. 腐蚀与防护, 2002, 23(2): 76-78 |
| |
| 作者姓名： | 刘建忠 |
| |
| 作者单位： | 协和石油化工集团,中国,有限公司,宁波,315803 |
| |
| 摘 要： | 针对4114工号不锈钢管道的开裂，进行原因分析，认为应力腐蚀和选材不当是主要原因，根据工况条件选用了新的钢材并采用了相应的措施，取得较好的效果。
|
| 关 键 词： | 不锈钢管道 应力腐蚀 选材 对策 化工管道 |
| 文章编号： | 1005-748X(2002)02-0076-03 |
| 修稿时间： | 2000-12-19 |
STRESS CORROSION CRACKING OF STAINLESS STEEL PIPE AND ITS COUNTERMEASURES |
| |
| LIU Jian zhong. STRESS CORROSION CRACKING OF STAINLESS STEEL PIPE AND ITS COUNTERMEASURES[J]. Corrosion & Protection, 2002, 23(2): 76-78 |
| |
| Authors: | LIU Jian zhong |
| |
| Abstract: | This article analyzes the causes of the stainless steel pipe cracking. The main reasons were stress corrosion and using unsuitable materials. According to the operation condition, selecting new proper materials and adoping other acceptable methods have got satisfactory results. |
| |
| Keywords: | Stainless steel pipe Stress corrosion Materials selection |