| 顶尖淬火开裂原因分析 |
| |
| 引用本文： | 燕样样. 顶尖淬火开裂原因分析[J]. 理化检验(物理分册), 2011, 0(9): 598-601 |
| |
| 作者姓名： | 燕样样 |
| |
| 作者单位： | 陕西工业职业技术学院材料工程系; |
| |
| 摘 要： | 采用宏观检验、金相检验、硬度测试及断口分析等方法,对万能工具磨床用大顶尖产生淬火开裂的原因进行了分析。结果表明:顶尖淬火开裂具有热应力型应力引起大型非淬透件形成纵劈和横断的特征。主要是顶尖中心部位的疏松、非金属夹杂物以及网状碳化物的存在降低了材料的脆断强度,淬火时热应力中的切向和轴向最大拉应力超过材料的脆断强度引起了顶尖开裂。
|
| 关 键 词： | 顶尖 淬火开裂 纵劈 横断 热应力 |
Analysis on Quenching Cracking in Sustain Top |
| |
| YAN Yang-yang. Analysis on Quenching Cracking in Sustain Top[J]. Physical Testing and Chemical Analysis Part A:Physical Testing, 2011, 0(9): 598-601 |
| |
| Authors: | YAN Yang-yang |
| |
| Affiliation: | YAN Yang-yang (Department of Material Engineering,Shaanxi Poly Technical Institute,Xianyang 712000,China) |
| |
| Abstract: | The reasons of quenching cracking in the big sustain top used in the universal grinder were analyzed through macroscopic inspection,metallographic examination,hardness testing and fracture analysis.The results showed that the cracking had the characteristics of longitudinal cracking and cross-sectional cracking in the large non-hardened parts.The critical reason was that there were loose,nonmetallic inclusions,serious netted carbide in the central of big sustain top,which weakened the strength of fragile sp... |
| |
| Keywords: | sustain top quenching cracking longitudinal cracking cross-sectional cracking thermal stress |
| 本文献已被 CNKI 维普 等数据库收录！ |
|