Calculation of the intrinsic dead layers thicknesses from Au/Ba0.5Sr0.5TiO3/Pt thin film capacitors

Ferroelectric Ba_0.5Sr_0.5TiO₃ (BST) films were prepared on Pt/Ti/SiO₂/Si substrates by the sol-gel process. The films were spin-coated at 2000 rpm for 30 secs and then pyrolysed for 5 mins at the temperature of 350^∘C. This coating procedure was repeated for 3, 4, 5 and 6 times to obtain BST films with different thicknesses. After coating the films with the desired repetition times, the films were finally annealed in a conventional furnace at temperatures ranging from 600^∘C to 800^∘C with a 50^∘C interval in between. The films obtained with an annealing procedure of 750^∘C were polycrystalline with the presence of an impurity BaCO₃ phase. The capacitance and leakage current were measured and used to extract information on the metal-BST interface. With the series capacitance model and modified Schottky emission equation, the thickness of the dead layers for Au/BST and Pt/BST interfaces were calculated to be less than 6 nm and 5 nm, respectively.