| 锌粉催化合成含硅芳炔树脂 |
| |
| 引用本文： | 沈浩,蒋孝杰,周燕,邓诗峰,杜磊,夏红娟,黄发荣. 锌粉催化合成含硅芳炔树脂[J]. 过程工程学报, 2014, 14(2): 329-334 |
| |
| 作者姓名： | 沈浩 蒋孝杰 周燕 邓诗峰 杜磊 夏红娟 黄发荣 |
| |
| 作者单位： | 华东理工大学材料科学与工程学院特种功能高分子材料及相关技术教育部重点实验室华东理工大学材料科学与工程学院特种功能高分子材料及相关技术教育部重点实验室华东理工大学材料科学与工程学院特种功能高分子材料及相关技术教育部重点实验室华东理工大学材料科学与工程学院特种功能高分子材料及相关技术教育部重点实验室华东理工大学材料科学与工程学院特种功能高分子材料及相关技术教育部重点实验室中国航天科技集团第八研究院802所华东理工大学特种功能高分子材料及其相关技术教育部重点实验室 |
| |
| 摘 要： | 以二乙炔基苯和二甲基二氯硅烷为原料，通过锌粉催化合成含硅芳炔树脂，确定了合成产物的结构. 结果表明，以乙腈为溶剂、锌粉过量200%、温度80℃、反应时间10 h为最佳反应条件，反应收率达82%以上；所制含硅芳炔树脂有良好的加工性能，在约170℃可发生交联固化反应；树脂的热稳定性良好，在N2气氛下失重5%时的温度为529℃，800℃时树脂残留率约为85%.
|
| 关 键 词： | 含硅芳炔树脂 锌粉 催化 耐高温树脂 |
| 收稿时间： | 2014-01-27 |
Synthesis of Silicon-containing Arylacetylene Resin Catalyzed by Zinc Powde |
| |
| SHEN HaoJIANG Xiao-jieZHOU YanDENG Shi-fengDU LeiXIA Hong-juanHUANG Fa-rong. Synthesis of Silicon-containing Arylacetylene Resin Catalyzed by Zinc Powde[J]. Chinese Journal of Process Engineering, 2014, 14(2): 329-334 |
| |
| Authors: | SHEN HaoJIANG Xiao-jieZHOU YanDENG Shi-fengDU LeiXIA Hong-juanHUANG Fa-rong |
| |
| Abstract: | Silicon-containing arylacetylene (PSA) resin was prepared by the condensation reaction between diethynylbenzene and dimethyldichlorosilane catalyzed by zinc powder. The structures of PSA resin were characterized. The optimum reaction conditions were obtained as follows: acetonitrile as solvent, amount of zinc overdosed 200%, temperature 80℃ and reaction time 10 h. And the resulting reaction yield reached up to 82%. The curing behavior of PSA resin was analyzed by DSC, and the thermal stability of cured resin by TGA. The results showed that the PSA resin was easily processed and could be cured at the temperature of about 170℃. The cured PSA resin possessed excellent thermal stability. The temperature at 5% weight loss reached 529℃, and char yield of the cured resin at 800℃ under nitrogen was 85%. |
| |
| Keywords: | PSA resin zinc powder catalysis heat-resistant resin |