High-Temperature Oxidation Behavior of (Ti,Cr)N Coating Deposited on 4Cr13 Stainless Steel by Multi-arc Ion Plating |
| |
Authors: | Cai Hangwei Gao Yuan Yuan Lin Ma Zhikang Wang Chenglei |
| |
Affiliation: | Guilin University of Electronic Technology, Guilin 541004, China |
| |
Abstract: | (Ti, Cr)N coatings were deposited on 4Cr13 stainless steel by multi-arc ion plating. High-temperature oxidation behaviors of (Ti1-xCrx)N (x=0.28, 0.56, 0.73) coatings with different chrome contents were investigated at 700 oC. And surface morphologies and surface compositions of oxidized coatings were also studied. Thermal analysis experiments of (Ti,Cr)N coatings were conducted by thermogravimetry (TG) and differential scanning calorimetry (DSC), and the results were compared with TiN coating. The results show that Cr content in the (Ti1-xCrx)N coating increases with the elevation of the arc current of Cr target, and a linear relation exists between Cr content and the ratio of arc current of Cr target and Ti target (ICr/ITi for short). The higher the Cr content is, the better the high-temperature oxidation resistance of (Ti1-xCrx)N coating is, and the oxidation thermodynamics temperatures of (Ti1-xCrx)N coating are higher than that of TiN coating, which indicates that the oxidation thermodynamic equilibrium temperature of the coating elevates observably with the addition of Cr |
| |
Keywords: | Cr content (Ti1-xCrx)N coating high-temperature oxidation behavior thermal analysis |
本文献已被 CNKI 等数据库收录! |
| 点击此处可从《稀有金属材料与工程》浏览原始摘要信息 |
|
点击此处可从《稀有金属材料与工程》下载全文 |
|