| 两种不同冶金工艺生产的60Si2CrVA弹簧钢的高周疲劳性能 |
| |
| 引用本文： | 郝立群,惠卫军,项金钟,惠荣,翁宇庆.两种不同冶金工艺生产的60Si2CrVA弹簧钢的高周疲劳性能[J].钢铁,2009,44(2):64-0. |
| |
| 作者姓名： | 郝立群 惠卫军 项金钟 惠荣 翁宇庆 |
| |
| 作者单位： | 1.云南大学物理科学技术学院， 云南 昆明 650091；2.钢铁研究总院先进钢铁材料技术国家工程研究中心， 北京 100081；3.江阴兴澄特种钢铁有限公司， 江苏 江阴 214429；4.中国金属学会， 北京 100711 |
| |
| 基金项目： | 国家重点基础研究发展规划项目(973)(2004CB619104) |
| |
| 摘 要： | 采用旋转弯曲疲劳试验研究了两种不同冶金工艺生产的60Si2CrVA弹簧钢的高周疲劳破坏行为。结果表明，尽管两种试验料的氧含量接近，但两者夹杂物特征的差异使其疲劳性能存在明显的差异。与采用电炉+LF+VD+CC工艺生产的X8料相比，采用转炉＋LF+RH+CC工艺生产的X6料中的夹杂物数量明显减少，夹杂物尺寸较小，同时还减少了不规则的多棱角富Al2O3夹杂，因而后者的疲劳强度得到明显提高，并具有良好的疲劳寿命稳定性。
|
| 关 键 词： | 冶金生产工艺 60Si2CrVA弹簧钢 高周疲劳 非金属夹杂物 |
High-Cycle Fatigue Properties of 60Si2CrVA Spring Steels Produced by Two Different Metallurgical Processes |
| |
| HAO Li-qun,HUI Wei-jun,XIANG Jin-zhong,HUI Rong,WENG Yu-qing.High-Cycle Fatigue Properties of 60Si2CrVA Spring Steels Produced by Two Different Metallurgical Processes[J].Iron & Steel,2009,44(2):64-0. |
| |
| Authors: | HAO Li-qun HUI Wei-jun XIANG Jin-zhong HUI Rong WENG Yu-qing |
| |
| Affiliation: | 1.School of Physical Science and Technology, Yunnan University, Kunming 650091, Yunnan, China;2.National Engineering Research Center of Advanced Steel Technology, Beijing 100081, China;3.Jiangyin Xingcheng Special Steel Co., Ltd., Jiangyin 214429, Jiangsu, China;4.The Chinese Society for Metals, Beijing 100711, China |
| |
| Abstract: | The high-cycle fatigue fracture behavior of 60Si2CrVA spring steels produced by two different metallurgical processes were studied by using rotating bar two-point bending fatigue machine.The experimental results indicate that the characteristics of the inclusions in these two steels were different,which was the main reason for the significant difference of their fatigue properties,although their oxygen content was almost equal.Compared with X8 steel produced by the metallurgical process of EAF+LF+VD+CC,the ... |
| |
| Keywords: | metallurgical process 60Si2CrVA spring steel high-cycle fatigue non-metallic inclusion |