Anatase-Type TiO2 and ZrO2-Doped TiO2 Directly Formed from Titanium(III) Sulfate Solution by Thermal Hydrolysis: Effect of the Presence of Ammonium Peroxodisulfate on their Formation and Properties

Anatase-type TiO₂ powder containing sulfur with absorption in the visible region was directly formed as particles with crystallite in the range 15–88 nm by thermal hydrolysis of titanium(III) sulfate (Ti₂(SO₄)₃) solution at 100°–240°C. Because of the presence of ammonium peroxodisulfate ((NH₄)₂S₂O₈), the yield of anatase-type TiO₂ from Ti₂(SO₄)₃ solution was accelerated, and anatase with fine crystallite was formed. Anatase-type TiO₂ doped with ZrO₂ up to 9.8 mol% was directly precipitated as nanometer-sized particles from the acidic precursor solutions of Ti₂(SO₄)₃ and zirconium sulfate in the presence and the absence of (NH₄)₂S₂O₈ by simultaneous hydrolysis under hydrothermal conditions at 200°C. By doping ZrO₂ into TiO₂ and with increasing ZrO₂ content, the crystallite size of anatase was decreased, and the anatase-to-rutile phase transformation was retarded as much as 200°C. The anatase-type structure of ZrO₂-doped TiO₂ was maintained after heating at 1000°C for 1 h. The favorable effect of doping ZrO₂ to anatase-type TiO₂ on the photocatalytic activity was observed.