The effect of atmospheric corona treatment on AA1050 aluminium |
| |
Authors: | M. Jariyaboon,P. Mø ller |
| |
Affiliation: | a Division of Materials Science and Engineering, Department of Mechanical Engineering, Technical University of Denmark, 2800 Kgs. Lyngby, Denmark b Center for Electron Nanoscopy, Technical University of Denmark, 2800 Kgs. Lyngby, Denmark c Center for Individual Nanoparticle Functionality, Department of Physics, Technical University of Denmark, 2800 Kgs. Lyngby, Denmark |
| |
Abstract: | The effect of atmospheric corona discharge on AA1050 aluminium surface was investigated using electrochemical polarization, SEM-EDX, FIB-SEM, and XPS. The corona treatment was performed with varying time (1, 5, and 15 min) in atmospheric air. A 200 nm oxide layer was generated on AA1050 after the 15 min air corona treatment. A significant reduction in anodic and cathodic reactivities was observed starting from 1 min exposure, which further decreased with prolonged exposure (15 min) and after delayed testing (after 30 days). The reduction in surface reactivity is due to the formation of thicker and denser oxide film. |
| |
Keywords: | A. Aluminium B. Polarization C. Oxide coatings |
本文献已被 ScienceDirect 等数据库收录! |
|