The influence of surface morphology of TiO2 coating on the performance of dye-sensitized solar cells

The optimization of solar energy conversion efficiency of dye-sensitized solar cells (DSSCs) was investigated by the tuning of TiO₂ photoelectrode's surface morphology. Double-layered TiO₂ photoelectrodes with four different structures were designed by the coating of TiO₂ suspension, incorporated with low and high molecular weight poly(ethylene glycol) as a binder. Among these four systems, P2P1, where P1 and P2 correspond to the molecular weight of 20,000 and 200,000, respectively, showed the highest efficiency under the conditions of identical film thickness and constant irradiation. This can be explained by the larger pore size and higher surface area of P2P1 TiO₂ electrode than the other materials as revealed by scanning electron microscopic (SEM) and Brunauer–Emmett–Teller (BET) analyses. Electrochemical Impedance Spectroscopy (EIS) analysis shows that P2P1 formulation displayed a smaller resistance than the others at the TiO₂/electrolyte interface. The best efficiency (η) of 9.04% with the short-circuit photocurrent density (J_sc) and open-circuit voltage (V_oc) of 18.9 mA/cm² and 0.74 V, respectively, was obtained for a solar cell by introducing the light-scattering particles to the TiO₂ nanoparticles matrix coated on FTO electrode having the sheet resistivity of 8 Ω/sq.