| Ag/ZnO纳米复合抗菌剂解团聚工艺及机制 | |
| 引用本文： | 孟阿兰,岑 伟,李镇江,郭 锋,耿在丹,张振华. Ag/ZnO纳米复合抗菌剂解团聚工艺及机制[J]. 稀有金属材料与工程, 2009, 38(2): 358-360 |
| 作者姓名： | 孟阿兰 岑 伟 李镇江 郭 锋 耿在丹 张振华 |
| 作者单位： | 1. 青岛科技大学生态化工教育部重点实验室,山东青岛,266042;青岛科技大学,山东青岛,266042 2. 青岛科技大学,山东青岛,266042 3. 郑州广播电视大学,河南郑州,450003 4. 青岛科技大学生态化工教育部重点实验室,山东青岛,266042 |
| 基金项目： | 国家自然科学基金，山东省自然科技学基金，山东省教育厅基金，山东省科技攻关项目 |
| 摘 要： | 采用沉降实验、激光粒度分布、透射电镜等手段,研究PVPK17对Ag/ZnO纳米复合抗菌剂的解团聚的影响及机制,同时采用最小抑菌浓度对解团聚前后的抗菌性能进行表征.结果表明:经PVPK:17解团聚后的Ag/ZnO纳米复合抗菌剂可在异丙醇中稳定悬浮6 d以上,分散后的Ag/ZnO纳米复合抗菌剂的平均粒度可达51.3 nm,当加入PVPK17的质量百分数为40%时达到最佳分散效果.用透射电镜观测表明,解团聚的Ag/ZnO纳米复合抗菌剂分散较好,在此基础上建立了PVPk17对Ag/ZnO纳米复合抗菌剂的解团聚模型.抗菌实验表明,分散后的Ag/ZnO纳米复合抗菌剂的MIC可达50mg/L,抗菌性能良好. |
| 关 键 词： | 解团聚 纳米复合抗菌剂 |
| 收稿时间： | 2008-01-24 |
Deaggregation Technology and Mechanism of Ag/ZnO Nano Composite Antibacterial Agent |
|
| Meng Alan,Cen Wei,Li Zhenjiang,Guo Feng,Geng Zaidan and Zhang Zhenhua. Deaggregation Technology and Mechanism of Ag/ZnO Nano Composite Antibacterial Agent[J]. Rare Metal Materials and Engineering, 2009, 38(2): 358-360 | |
| Authors: | Meng Alan Cen Wei Li Zhenjiang Guo Feng Geng Zaidan Zhang Zhenhua |
| Affiliation: | 1. Key Laboratory of Eco-Chemical Engineering;Ministry of Education;Qingdao University of Science and Technology;Qingdao 266042;China;2. Qingdao University of Science and Technology;China;3. Zhengzhou Radio and Television University;Zhengzhou 450003;China |
| Abstract: | In this paper, a deaggregation technology and its mechanism were studied for the Ag/ZnO nanocomposite antibacterial agent added with PVPK17 by sedimentation experiment, laser scattering particle size analysis and transmission electron microscopy (TEM). The minimum inhibitory concentration of the fore-aft deaggregation Ag/ZnO nanocomposite antibacterial agent was tested. The results showed that the Ag/ZnO nanocomposite antibacterial agent in isopropanol could be stable suspension more than 6 days after deagg... |
| Keywords: | PVP Ag/ZnO |