Development of ultrafine lamellar structures in two-phase γ-TiAl alloys
Authors:P. J. Maziasz  C. T. Liu
Affiliation:(1) Metals and Ceramics Division, Oak Ridge National Laboratory, the Alloying Behavior and Design Group, 37831-6115 Oak Ridge, TN
Abstract:Processing of two-phase γ-TiAl alloys (Ti-47Al-2Cr-2Nb, or minor modifications thereof) above the α-transus temperature (T α ) produced unique refined-colony/ultrafine lamellar structures in both powder-and ingot-metallurgy (PM and IM, respectively) alloys. These ultrafine lamellar structures consist of fine laths of the γ and α 2 phases, with average interlamellar spacings (λ L ) of 100 to 200 nm and α 2-α 2 spacings (λ α ) of 200 to 500 nm, and are dominated by γ/α 2 interfaces. This characteristic microstructure forms by extruding PM Ti-47Al-2Cr-2Nb alloys at 1400 °C and also forms with finer colony size but slightly coarser, fully lamellar structures by hot-extruding similar IM alloys. Alloying additions of B and W refine λ L and λ α in both IM Ti-47Al (cast and heat treated at 1400 °C) and IM Ti-47Al-2Cr-2Nb alloys (extruded at 1400 °C). The ultrafine lamellar structure in the PM alloy remains stable during heat treatment at 900 °C for 2 hours but becomes unstable after 4 hours at 982 °C; the ultrafine lamellar structure remains relatively stable after aging for >5000 hours at 800 °C. Additions of B+W dramatically improve the coarsening resistance of λ L and λ α in the IM Ti-47Al alloys aged for 168 hours at 1000 °C. In both the PM and IM Ti-47Al-2Cr-2Nb alloys, these refined-colony/ultrafine lamellar structures correlate with high strength and good ductility at room temperature, and very good strength at high temperatures. While refining the colony size improves the room-temperature ductility, alloys with finer λ L are stronger at both room and high temperatures. Additions of B + W produce finer as-processed λ L and λ α in IM TiAl alloys and stabilize such structures during heat treatment or aging. This article is based on a presentation made in the symposium “Fundamentals of Gamma Titanium Aluminides,” presented at the TMS Annual Meeting, February 10–12, 1997, Orlando, Florida, under the auspices of the ASM/MSD Flow & Fracture and Phase Transformations Committees.
Keywords:
本文献已被 SpringerLink 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号