Preparation and studies of Eu and Tb co-doped Gd2O3 and Y2O3 sol-gel scintillating films

Eu³⁺ (2.5 at.%) and Tb³⁺ (0.005-0.01 at.%) co-doped gadolinium and yttrium oxide (Gd₂O₃ and Y₂O₃) powders and films have been prepared using the sol-gel process. High density and optical quality thin films were prepared with the dip-coating technique. Gadolinium (III) 2,4-pentadionate and yttrium (III) 2,4-pentadionate were used as precursors, and europium and terbium in their nitrate forms were used as doping agents. Chemical and structural analyses (infrared spectroscopy, X-ray diffraction and high-resolution transmission electron microscopy) were conducted on both sol-gel precursor powders and dip-coated films. The morphology of thin films heat-treated at 700 °C was studied by means of atomic force microscopy. It was shown that the highly dense and very smooth films had a root mean roughness (RMS) of 2 nm ± 0.2 (A = 0.0075 Tb³⁺) and 24 nm ± 3.0 (B = 0.01 Tb³⁺). After treatment at 700 °C, the crystallized films were in the cubic phase and presented a polycrystalline structure made up of randomly oriented crystallites with grain sizes varying from 20 to 60 nm. The X-ray induced emission spectra of Eu³⁺- and Tb³⁺-doped Gd₂O₃ and Y₂O₃ powders showed that Tb³⁺ contents of 0.005, 0.0075 and 0.01 at.% affected their optical properties. Lower Tb³⁺ concentrations (down to 0.005 at.%) in both systems enhanced the light yield.