A material and environment-dependent criterion for the prediction of fatigue crack paths in metallic structures |
| |
Authors: | V ronique Doquet,Graciela Bertolino |
| |
Affiliation: | aLaboratoire de Mécanique des Solides, UMR CNRS 7649, Ecole Polytechnique, 91128 Palaiseau cedex, France |
| |
Abstract: | Crack growth under mode II cyclic loading was investigated in maraging steel, ferritic–pearlitic steel and TA6V. When ΔKII exceeds a threshold value, cracks do not bifurcate but grow in mode II over a distance which increases with ΔKII. Shear mode crack growth was much more extensive in maraging steel than in TA6V and ferritic–pearlitic steel. This result is discussed in relation with the cyclic behaviour of the materials and the importance of friction along the crack faces. The maximum growth rate criterion is shown to be suitable for the prediction of crack paths when shear mode crack growth is likely to occur. |
| |
Keywords: | Fatigue Crack Mode II Friction Bifurcation |