| 高强水基环氧砂浆的研制 |
| |
| 引用本文： | 景惧斌,罗毅.高强水基环氧砂浆的研制[J].硅酸盐通报,2009,28(2):385-387. |
| |
| 作者姓名： | 景惧斌 罗毅 |
| |
| 作者单位： | 天地金草田,北京,科技有限公司,北京,100013 |
| |
| 摘 要： | 研制开发了一种高强水性环氧乳液砂浆,确定了水性环氧乳液砂浆的基本组成:水性环氧乳液掺量为5%,促进剂掺量1.25%(相水性环氧乳液的质量百分比),消泡剂掺量为0.3%(水性环氧乳液的质量百分比),并在此基础上加入适量的高效减水剂和保水增稠剂,最终得到了一种性能优良的水性环氧乳液砂浆.
|
| 关 键 词： | 水性环氧树脂 粘结强度 抗压强度 抗折强度 |
Research on the Waterborne Epoxy Resin High Strength Mortar |
| |
| JING Ju-bin,LUO Yi.Research on the Waterborne Epoxy Resin High Strength Mortar[J].Bulletin of the Chinese Ceramic Society,2009,28(2):385-387. |
| |
| Authors: | JING Ju-bin LUO Yi |
| |
| Abstract: | A new kind of waterborne epoxy resin high strength mortar was developed. The final component of mortar was confirmed. The results showed that when the waterborne epoxy resin emulsion content was 5%-10%,the curing accelerator content was 1.25%(the mass percentage ratio of waterborne epoxy resin emulsion) and the antifoam agent content was 0.3% (the mass percentage ratio of waterborne epoxy resin emulsion),an excellent waterborne epoxy resin mortar was gotten in the presence of high efficiency water reducing ... |
| |
| Keywords: | waterborne epoxy resin binding strength compressive strength bending strength |