Analytical and experimental studies on fatigue crack path under complex multi-axial loading |
| |
Authors: | L. REIS B. LI M. DE FREITAS |
| |
Affiliation: | Department of Mechanical Engineering, Instituto Superior Técnico, Av. Rovisco Pais, 1049-001, Lisboa, Portugal |
| |
Abstract: | In real engineering components and structures, many accidental failures are due to unexpected or additional loadings, such as additional bending or torsion, etc. Fractographical analyses of the failure surface and the crack orientation are helpful for identifying the effects of the non‐proportional multi‐axial loading. There are many factors that influence fatigue crack paths. This paper studies the effects of multi‐axial loading path on the crack path. Two kinds of materials were studied and compared in this paper: AISI 303 stainless steel and 42CrMo4 steel. Experiments were conducted in a biaxial testing machine INSTRON 8800. Six different biaxial loading paths were selected and applied in the tests to observe the effects of multi‐axial loading paths on the additional hardening, fatigue life and the crack propagation orientation. Fractographic analyses of the plane orientations of crack initiation and propagation were carried out by optical microscope and SEM approaches. It was shown that the two materials studied had different crack orientations under the same loading path, due to their different cyclic plasticity behaviour and different sensitivity to non‐proportional loading. Theoretical predictions of the damage plane were made using the critical plane approaches such as the Brown–Miller, the Findley, the Wang–Brown, the Fatemi–Socie, the Smith–Watson–Topper and the Liu's criteria. Comparisons of the predicted orientation of the damage plane with the experimental observations show that the critical plane models give satisfactory predictions for the orientations of early crack growth of the 42CrMo4 steel, but less accurate predictions were obtained for the AISI 303 stainless steel. This observation appears to show that the applicability of the fatigue models is dependent on the material type and multi‐axial microstructure characteristics. |
| |
Keywords: | fatigue crack path fatigue life prediction fractographic analysis multi-axial fatigue proportional and non-proportional loading |
|
|