Dielectric Characteristics of Ba_(0.65)Sr_(0.35)TiO_3 Thin Films by Sol-Gel Method

Ferroelectric Ba0.65Sr0.35TiO3(BST) thin films on the Pt/Ti/SiO2/Si substrate have been successfully prepared by sol-gel. Such films have approximately 300 nm thicknesses with a remnant polarization of about 2.95 μC/cm2 and a coercive field of about 21.5 kV/cm. The investigations of X-ray diffraction and atomic force microscopy show that the BST films annealed at 650 °C exhibit a tetragonal structure and that the films dominantly consist of large column or grains of about 89 nm in diameter. The curves of the temperature dependence of dielectric coefficient in different frequencies display the curie transition at the temperature around 23 °C. The dielectric loss tangent of BST thin films at 100 kHz is less than 0.04. As a result,the BST thin films are more applicable for fabrication of infrared detector compared with the BST thin films reported previously.

Dielectric Characteristics of Ba0.65Sr0.35TiO3 Thin Films by Sol-Gel Method

Ferroelectric Ba0.6sSr0.3sTiO3 (BST) thin films on the Pt/Ti/SiO2/Si substrate have been successfully prepared by sol-gel. Such films have approximately 300 nm thicknesses with a remnant polarization of about 2.95 μC/cm2 and a coercive field of about 21.5 kV/cm. The investigations of X-ray diffraction and atomic force microscopy show that the BST films annealed at 650 ℃ exhibit a tetragonal structure and that the films dominantly consist of large column or grains of about 89 nm in diameter. The curves of the temperature dependence of dielectric coefficient in different frequencies display the curie transition at the temperature around 23 ℃.The dielectric loss tangent of BST thin films at 100 kHz is less than 0.04. As a result, the BST thin films are more applicable for fabrication of infrared detector compared with the BST thin films reported previously.