Low-temperature sintered pollucite ceramic from geopolymer precursor using synthetic metakaolin |
| |
Authors: | Peigang He Dechang Jia |
| |
Affiliation: | 1. HIT Science Park, Institute for Advanced Ceramics, Harbin Institute of Technology, No. 2 Yikuang Street, P.O. Box 3022, Harbin, 150080, People’s Republic of China
|
| |
Abstract: | In this article, pollucite ceramic with high relative density and low coefficient of thermal expansion (CTE) was prepared from Cs-based geopolymer using synthetic metakaolin. Crystallization and sintering behavior of the Cs-based geopolymer together with thermal expansion behavior of the resulted pollucite ceramic were investigated. On heating at 1200 °C for 2 h, the amorphous Cs-based geopolymer completely crystallized into pollucite based on crystal nucleation and growth mechanism. Selected area diffraction analysis and XRD results confirmed the resulted pollucite ceramic at room temperature was pseudo-cubic phase with superlattice structure. Compared with Cs-based geopolymer using natural metakaolin, geopolymer using synthetic metakaolin in this article showed a much lower viscous sintering temperature range, which started at 800 °C, reached a maximum value of ?7.47 × 10?4/°C at 1121.9 °C, and ended at 1200 °C. Cesium volatilization appeared only when temperature was above 1250 °C. Therefore, densified pollucite ceramic can be prepared from Cs-based geopolymer using synthetic metakaolin without cesium volatilization. Abnormal thermal shrinkage of pollucite ceramic was observed at temperature range from 25.3 to 54.6 °C because of pseudo-cubic to cubic phase transition, and its average CTE was 2.8 × 10?6/°C from 25 to 1200 °C. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|