| 20Cr2MoV钢焊缝金属微观分析 |
| |
| 引用本文： | 余圣甫,李志远,刘顺洪,王杰. 20Cr2MoV钢焊缝金属微观分析[J]. 物理测试, 2000, 0(5): 19-22 |
| |
| 作者姓名： | 余圣甫 李志远 刘顺洪 王杰 |
| |
| 作者单位： | 1. 华中理工大学,武汉,430074
2. 南通商检局,220062 |
| |
| 摘 要： | ２０Ｃｒ２ＭｏＶ高强度热强钢用埋弧自动焊进行多道多层焊，经调质热处理后，焊缝金属的冲击性值急剧下降，不能满足使用要求。用扫描电镜分析的结果表明：焊缝金属中有较多的非金属夹杂物，特别是夹杂物附近存在微裂纹及晶界碳化物析出是造成焊缝金属低温冲击韧性值低的主要原因。
|
| 关 键 词： | 20Cr2MoV钢 焊缝金属 非金属夹杂物 微观分析 |
| 修稿时间： | 1999-10-22 |
Microanalysis of Welding Metal in 20Cr2MoV Steel |
| |
| Yu Shengfu,Li Zhiyuan,Liu Shunhong,Wang Jie. Microanalysis of Welding Metal in 20Cr2MoV Steel[J]. Physics Examination and Testing, 2000, 0(5): 19-22 |
| |
| Authors: | Yu Shengfu Li Zhiyuan Liu Shunhong Wang Jie |
| |
| Abstract: | 20Cr2MoV high strength heat resistance steel had been welded in multilayer and multi-pass for submerged arc welding. While the weld metals were quenched and tempered, the low temperature impact values of weld metals rapidly became bw and the properties of wld metals did not meet to need. The results analysing with scanning electron microscope show that non metallic inclusions in weld metals, microcracks around inclusions and carbides at grain boundaries make that the low temperature impact toughness values of weld metals rapidly became low. |
| |
| Keywords: | 20Cr2MoV steel weld metal non-metallic inclusion impact toughness |