| 2Cr13马氏体不锈钢铸坯表面纵裂控制 |
| |
| 引用本文： | 张卫红. 2Cr13马氏体不锈钢铸坯表面纵裂控制[J]. 连铸, 2007, 0(6): 39-40 |
| |
| 作者姓名： | 张卫红 |
| |
| 作者单位： | 太钢不锈钢股份有限公司第二炼钢厂,太原,030003 |
| |
| 摘 要： | 根据马氏体不锈钢在连铸浇注过程中的凝固收缩特性,分析连铸浇注过程中易引发表面纵裂的原因,提出应对措施,从而有效地避免板坯表面纵裂的产生.
|
| 关 键 词： | 板坯表面 纵裂 马氏体不锈钢 |
Improvement on slab surface quality for 2Cr13 martensitic stainless steel |
| |
| ZHANG Weihong. Improvement on slab surface quality for 2Cr13 martensitic stainless steel[J]. CONTINUOUS CASTING, 2007, 0(6): 39-40 |
| |
| Authors: | ZHANG Weihong |
| |
| Abstract: | Based on the slab solidification and shrinkage characteristics of martensitic stainless steel, the causes which induce the surface longitudinal cracking, were analyzed. Countermeasures were put forward and performed to avoid surface longitudinal cracking on slabs effectively. |
| |
| Keywords: | slab surface longitudinal cracking martensitie stainless steel |
| 本文献已被 维普 万方数据 等数据库收录！ |
|