Stripe and bubble domains in CoCr films

Using the colloid-scanning-electron-microscope (SEM) method, an investigation was conducted of the domain structure of CoCr films (400-1740 nm thick) at different points of the hysteresis loop. In some cases, an AC field exceeding the value of the coercive force was applied in addition to the DC field. For low-coercivity samples (H_c/H_k~0.02) a bubble structure, which is energetically more favorable above a certain critical field, was observed. From the dependence of the bubble density on the DC field the value of the anhysteretic collapse field was estimated and compared with the theory. Attempts were made to observe the field dependence of the domain structure of high-coercivity samples (H_c/ H_k~0.08) with different thicknesses. For one sample the results were compared with those determined using the Kerr effect. For thicker films the colloid-SEM method permits the simultaneous observation of the magnetic domains and the columnar structure at the surface of the sample