Re-evaluation of the phase relationship between plutonium and zirconium dioxides

The phase relationship between ZrO₂ and PuO₂ was examined in a low PuO₂ content region, from 3.1 to 11.2 mol% PuO₂, at temperatures between 1273 K and 1473 K, by high temperature X-ray diffractometry. The measurements were carried out in air. At 1273 K, the samples in this composition range consisted of two phases, monoclinic and cubic. Another phase, tetragonal, was observed at 1373 K. The low temperature monoclinic phase disappeared at 1473 K. It was confirmed that the monoclinic phase disappears around 1463 K; the disappearance temperature does not depend on the composition of the sample. It was, thus, inferred that there should be a eutectoid line in the phase diagram. Though the eutectoid point is not clear, the PuO₂ content at the point should be less than 3.1 mol%.