Structural and electrical properties of Cr-doped SrTiO3 porous materials

Series of single-phase materials with assumed formula SrTi_1?xCr_xO₃ (where x = 0, 1, 4, 6 mol.%) were obtained by sol-gel method. The structure and microstructure of materials were characterised by X-ray diffraction and scanning electron microscopy methods. Moreover, the study of electrical properties and evaluation of chemical stability in CO₂/H₂O atmosphere was performed by electrochemical impedance spectroscopy and thermogravimery methods, respectively. The possibility of participation of Cr-doped strontium titanate in oxidation–reduction processes was analysed by temperature-programed reduction (TPR) and temperature-programed oxidation (TPOx) measurements. The changes of lattice parameters together with XPS analysis, the Seebeck coefficient measurements results and TPR profiles obtained for SrTi_1?xCr_xO₃ materials prove the presence of chromium on +3 and +6 oxidation stages. Thus, chromium can be treated as both acceptor- and donor-type dopant in the SrTiO₃ structure. The Cr³⁺/Cr⁶⁺ ratio strongly affects the electrical properties, as the change of conduction mechanism was observed. The results of performed stability test clearly indicate that incorporation of chromium into SrTiO₃ structure results with decrease of chemical stability in CO₂ atmosphere.