Experimental investigation and analysis of a new photoelectrochemical reactor for hydrogen production

In this research paper, an experimental investigation of photoactive material titanium dioxide (TiO₂) coated on 180 cm² 316 stainless steel anode is undertaken to study the photoresponse on photoelectrochemical (PEC) hydrogen production. The TiO₂ nanoparticles are first prepared via sol-gel method. A large surface 316 stainless steel anode is coated with TiO₂ nanoparticles by a dip coating apparatus at a withdraw rate of 2.5 mm/s. The nanoparticles are carried on the stainless steel substrate by two-step annealing procedure. The potentiostatic studies confirm the photoactivity of TiO₂ nanoparticles in a photoelectrochemical reactor when exposed to solar ultraviolet (UV) light. The photon to current efficiency measurements carried out on the PEC reactor with TiO₂ coated large surface stainless steel as photoanode demonstrate a significant increase of photoresponse in UV light compared to the uncoated stainless steel prepared under similar conditions. Upon illumination at a power density of 600 W/m², the hydrogen production is observed in TiO₂ coated stainless steel substrate at a measured rate of 51 ml/h while no illumination conditions show a production rate of 42 ml/h. In comparative assessments, the TiO₂ coated substrate shows an increase in photocurrent of 10 mA with an energy efficiency of 1.32% and exergy efficiency of 3.42% at an applied potential of 1.6 V. The present results show a great potential for titanium nanoparticles semiconductor metal oxide in photoelectrochemical hydrogen production application.