Studies in the System Li2O–Al2O3–Fe2O3-H2O

Subsolidus equilibrium relations in a portion of the system Li2O-Fe₂O₃-Al₂O3 in the temperature range 500° to 1400°C. have been determined near po₂ = 0.21. Of particular interest in this system is the LiFe₅O₈-LiAl₅O₈ join, which shows complete solid solution above 1180°C. Below this temperature the solid solution exsolves into two spinel phases. At 600°C. approximately 15 mole % of each compound is soluble in the other. The high-temperature solid solution and the low-temperature exsolution dome extend into the ternary system from the 1:5 join. There is no appreciable crystalline solubility of LiFeO₂ or of α-Fe₂O₃ in LiFe₅O₈. An attempt to confirm HFe₅O₈ as the correct formulation of the magnetic ferric oxide "γ-Fe₂O₃" was inconclusive, but in the absence of positive evidence, the retention of γ-Fe₂O₃ is recommended. All the metallic oxides of the Group IV elements increase the temperature of the monotropic conversion of -γ-Fe₂O₃ to α-Fe₂O₃. Silica and thoria have a greater effect on this conversion than does titania or zirconia.