Versatility of a succinimidyl‐ester functional alkoxyamine for controlling acrylonitrile copolymerizations

Styrene/acrylonitrile (S/AN) and tert‐butyl methacrylate/acrylonitrile (tBMA/AN) copolymers were synthesized in a controlled manner (low polydispersity $ {{\overline M _w } / {\overline M _n }} $ with linear growth of number average molecular weight $ \overline M _n $ vs. conversion X) by nitroxide mediated polymerization (NMP) with a succinimidyl ester (NHS) terminated form of BlocBuilder unimolecular initiator (NHS‐BlocBuilder) in dioxane solution. No additional free nitroxide (SG1) was required to control the tBMA‐rich copolymerizations with NHS‐BlocBuilder, a feature previously required for methacrylate polymerizations with BlocBuilder initiators. Copolymers from S/AN mixtures (AN molar initial fractions f_AN,0 = 0.13–0.86, T = 115°C) had $ {{\overline M _w } / {\overline M _n }} $ = 1.14–1.26 and linear $ \overline M _n $ versus conversion X up to X ≈ 0.6. tBMA/AN copolymers (f_AN,0 = 0.10–0.81, T = 90°C) possessed slightly broader molecular weight distributions ( $ {{\overline M _w } / {\overline M _n }} $ = 1.23–1.50), particularly as the initial composition became richer in tBMA, but still exhibited linear plots of $ \overline M _n $ versus conversion X up to X ≈ 0.6. A S/AN/tBMA terpolymerization (f_AN,0 = 0.50, f_S,0 = 0.40) was also conducted at 90°C and revealed excellent control with $ \overline M _n $ = 13.6 kg/mol, $ {{\overline M _w } / {\overline M _n }} $ = 1.19, and linear $ \overline M _n $ versus conversion X up to X = 0.54. Incorporation of AN and tBMA in the final copolymer (molar composition F_AN = 0.47, F_tBMA = 0.11) was similar to the initial composition and represents initial designs to make tailored, acid functional AN copolymers by NMP for barrier materials. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013