Synthesis and properties of novel alicyclic‐functionalized polyimides prepared from natural—(D)‐camphor |
| |
Authors: | Hengsheng Zhang Juan Li Zhilin Tian Feng Liu |
| |
Affiliation: | Department of Chemistry, Nanchang University, Nanchang, Jiangxi 330031, People's Republic of China |
| |
Abstract: | In this article, a new alicyclic‐functionalized diamine, 1,3‐bis(4‐aminophenoxymethylene)‐1,2,2‐trimethylclopentane (BAMT) was successfully synthesized starting from natural —(D)‐camphor through four reaction steps of oxidation to offer a dicaboxylic acid, reduction to offer a diol, nucleophilic substitution to give a dinitro compound and then reduction to give the final diamine. Two alicyclic‐containing polyimides were prepared by polycondensing BAMT with 3,3′,4,4′‐biphenyltetracarboxylic dianhydride (BPDA) and 4,4′‐oxydiphthalicanhydride (ODPA), respectively. For the studies of the structure–property relationships of the polyimides, one aromatic polyimide of 4, 4′‐oxydianiline (ODA) polycondensed with ODPA was prepared in comparison. The alicyclic‐containinig polyimides PI (BPDA‐BAMT) and PI (ODPA‐BAMT) maintain good thermal properties with glass transition temperatures (Tg) of 257°C and 240°C, and temperatures at 5% weight loss (T5) of 443°C and 436°C in nitrogen, respectively. The alicyclic polyimides exhibit tensile strengths of 91.9–133 MPa, Young's moduli of 2.75—3.24 GPa, and elongations at break of 5.6–18%. Compared with the aromatic polyimide PI (ODPA‐ODA), PI (ODPA‐BAMT) shows improved transparency with the UV‐Vis transmittance at 500 nm over 80%. In addition, PI (ODPA‐BAMT) displays better solubility than PI (ODPA‐ODA), which has been confirmed by the bigger d‐spacing value of PI (ODPA‐BAMT) than that of PI (ODPA‐ODA) calculated from the Wide‐angle X‐ray Diffraction spectra. This study indicates that the renewable forestry compound, such as natural —(D)‐camphor, could be a good origin for the structural designing and preparation of alicyclic‐containing polyimides with outstanding combined features suitable for advanced microelectronic and optoelectronic applications. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013 |
| |
Keywords: | polyimides films thermoplastics |
|
|