Effects of Undercooling and Cooling Rate on Peritectic Phase Crystallization Within Ni-Zr Alloy Melt

The liquid Ni-16.75 at. pct Zr peritectic alloy was substantially undercooled and containerlessly solidified by an electromagnetic levitator and a drop tube. The dependence of the peritectic solidification mode on undercooling was established based on the results of the solidified microstructures, crystal growth velocity, as well as X-ray diffraction patterns. Below a critical undercooling of 124 K, the primary Ni₇Zr₂ phase preferentially nucleates and grows from the undercooled liquid, which is followed by a peritectic reaction of Ni₇Zr₂+L → Ni₅Zr. The corresponding microstructure is composed of the Ni₇Zr₂ dendrites, peritectic Ni₅Zr phase, and inter-dendritic eutectic. Nevertheless, once the liquid undercooling exceeds the critical undercooling, the peritectic Ni₅Zr phase directly precipitates from this undercooled liquid. However, a negligible amount of residual Ni₇Zr₂ phase still appears in the microstructure, indicating that nucleation and growth of the Ni₇Zr₂ phase are not completely suppressed. The micromechanical property of the peritectic Ni₅Zr phase in terms of the Vickers microhardness is enhanced, which is ascribed to the transition of the peritectic solidification mode. To suppress the formation of the primary phase completely, this alloy was also containerlessly solidified in free fall experiments. Typical peritectic solidified microstructure forms in large droplets, while only the peritectic Ni₅Zr phase appears in smaller droplets, which gives an indication that the peritectic Ni₅Zr phase directly precipitates from the undercooled liquid by completely suppressing the growth of the primary Ni₇Zr₂ phase and the peritectic reaction due to the combined effects of the large undercooling and high cooling rate.