| 冷拉拔珠光体钢丝的组织结构和残余应力(英文) |
| |
| 引用本文： | 杨帆,蒋建清,方峰,王燕.冷拉拔珠光体钢丝的组织结构和残余应力(英文)[J].稀有金属材料与工程,2010,39(Z1). |
| |
| 作者姓名： | 杨帆 蒋建清 方峰 王燕 |
| |
| 作者单位： | 1. 东南大学,江苏,南京,210096;江苏先进金属材料重点实验室,江苏,南京,211189
2. 江苏先进金属材料重点实验室,江苏,南京,211189 |
| |
| 基金项目： | National Natural Science Foundation of China，Jiangsu Planned Projects for Postdoctoral Research Funds，China Postdoctoral Science Foundation Funded Project，National Basic Research Program of China |
| |
| 摘 要： | 采用扫描电子显微镜和X射线衍射技术,分别研究了珠光体钢在冷拉拔过程中的组织结构和残余应力演化。随着拉拔应变量的增大,珠光体团逐渐转向拉拔方向。影响珠光体钢丝屈服应力和抗拉强度的关键因素是珠光体片层间距,它们之间满足Hall-Petch公式,通过拉伸试验求得其中k值为567.4kN·m-3/2。钢丝残余应力的X射线衍射测量结果表明,随着应变量增加,钢丝的应力增大,这与拉拔过程中的加工硬化有关。
|
| 关 键 词： | 拉拔 珠光体钢 Hall-Petch关系 残余应力 |
Microstructure and Residual Stress of Cold Drawn Pearlitic Wires |
| |
| Yang Fan,Jiang Jianqing,Fang Feng,Wang Yan.Microstructure and Residual Stress of Cold Drawn Pearlitic Wires[J].Rare Metal Materials and Engineering,2010,39(Z1). |
| |
| Authors: | Yang Fan Jiang Jianqing Fang Feng Wang Yan |
| |
| Affiliation: | Yang Fan1,2,Jiang Jianqing2,Fang Feng2,Wang Yan2 (1.Southeast University,Nanjing 210096,China) (2.Jiangsu Key Laboratory of Advanced Metallic Materials,Nanjing 211189,China) |
| |
| Abstract: | Microstructure and residual stress evolution of pearlitic steel during cold drawing was investigated by scanning electron microscope and X-ray diffraction, respectively. With drawing strain increasing, the pearlitic colonies gradually aligned to the drawing direction. It was found that the key factor affecting the flow stress and ultimate tensile strength of drawing rods was the interlamellar spacing of pearlite, in which a Hall-Petch relationship with the parameter k of 567.4 kN·m-3/2 was established through tensile tests. The XRD results indicated that a work hardening mechanism was contributed to the increasing residual stress in the cold-drawn rods with increasing drawing strain. |
| |
| Keywords: | cold drawing pearlitic steel Hall-Petch relationship residual stress |