Improving the mechanical properties of Al2O3/Ni laminated composites by adding Ni particles in Al2O3 layers

The (Al₂O₃ + Ni) composite, (Al₂O₃ + Ni)/Ni and Al₂O₃/(Al₂O₃ + Ni)/Ni laminated materials were prepared by aqueous tape casting and hot pressing. Results indicated that the (Al₂O₃ + Ni) composite had higher strength and fracture toughness than those of pure Al₂O₃. The fracture toughness of (Al₂O₃ + Ni)/Ni and Al₂O₃/(Al₂O₃ + Ni)/Ni laminated materials was higher than not only those of pure Al₂O₃, but also those of Al₂O₃/Ni laminar with the same layer numbers and thickness ratio. It was found that the toughness of the Al₂O₃/(Al₂O₃ + Ni)/Ni laminated material with five layers and layer thickness ratio = 2 could reach 16.10 MPa m^1/2, which were about 4.6 times of pure Al₂O₃. The strength and toughness of the (Al₂O₃ + Ni)/Ni laminated material with three layers and layer thickness ratio = 2 could reach 417.41 MPa and 12.42 MPa m^1/2. It indicated the material had better mechanical property.