Susceptibility to Hot Cracking and Weldment Heat Treatment of Haynes 230 Superalloy |
| |
Authors: | CMCheng CPChou IKLee ICKuo |
| |
Affiliation: | Department of Mechatronic Technology, National Taiwan Normal University, Taipei, Taiwan, China |
| |
Abstract: | This study investigates the susceptibility of hot cracking and weldment heat treatment of Haynes 230 superalloy.The Varestriant test was conducted to evaluate this susceptibility. Welding was performed by gas tungsten arc welding(GTAW)and plasma arc welding(PAW)with stress relief heat treatment and solid solution heat treatment. A tensile test is then performed to measure the changes in the mechanical properties of the heattreated material. The results indicate that the number of thermal cycles does not affect the susceptibility of Haynes 230 superalloy to hot cracking. However, it does increase the strain. In weldment of heat treatment,stress relief annealing increases the yield strength and tensile strength of the welded parts. The section of the tensile specimens shows fibrous fractures on the welded parts, regardless of whether they are heat-treated. |
| |
Keywords: | Haynes 230 super alloy Varestriant test Hot cracking Susceptibility Stress relief annealing |
本文献已被 CNKI 维普 万方数据 等数据库收录! |
| 点击此处可从《材料科学技术学报》浏览原始摘要信息 |
|
点击此处可从《材料科学技术学报》下载全文 |