| 邯钢200万t/a链篦机-回转窑投产初期生球爆裂的原因及解决方案 |
| |
| 引用本文： | 张化明,曾才兵,张磊晶,万义东.邯钢200万t/a链篦机-回转窑投产初期生球爆裂的原因及解决方案[J].烧结球团,2006,31(3):42-44. |
| |
| 作者姓名： | 张化明 曾才兵 张磊晶 万义东 |
| |
| 作者单位： | 056015,河北,邯郸钢铁公司炼铁部 |
| |
| 摘 要： | 介绍了邯钢200万t/a球团生产线达产过程中出现的生球爆裂问题及解决方法和实际效果.
|
| 关 键 词： | 链篦机-回转窑球团 生球爆裂 造球 |
| 收稿时间： | 2006-02-17 |
| 修稿时间： | 2006-02-17 |
REASONS OF GREEN PELLET CRACKING AND MEASURES OF PREVENT CRACKING IN HANGGANG PELLET PRODUCTION |
| |
| Zhang Huaming.REASONS OF GREEN PELLET CRACKING AND MEASURES OF PREVENT CRACKING IN HANGGANG PELLET PRODUCTION[J].Sintering and Pelletizing,2006,31(3):42-44. |
| |
| Authors: | Zhang Huaming |
| |
| Affiliation: | Zhang Huaming et al. |
| |
| Abstract: | Pointed at the problem of green pellet cracking during the drying and preheating in HANGGANG grate-kiln pelletizing line commissioning, the reasons were analyzed and some measures to prevent the green pellet cracking was adopted. As a result, the green pellet cracking problem was solved effectively and the product pellet quality was improved. |
| |
| Keywords: | grate-kiln pelletizing process green pellet cracking bailing |