Formation and characterisation of a chromate conversion coating on AA6060 aluminium

AA6060-T6, an AlMg0.5Si0.4 model alloy and α-Al(Fe,Mn)Si phase electrodes have been subjected to chromate treatment in a commercial chromate-fluoride based solution. The coated surfaces were subsequently examined by use of field emission SEM, TEM, AES and electrochemical measurements in 0.1 M NaCl solution in order to study the effect of substrate microstructure on coating formation and properties. Non-uniform growth of the chromate conversion coating (CCC) on AA6060-T6 resulted in a porous morphology, with cracks extending down to the base metal. Poor coverage was particularly observed at the grain boundaries. The thickness of the CCC after completed treatment was about 150-200 nm, while significantly thinner films were formed on the α-Al(Fe,Mn)Si particles. AlMg0.5Si0.4 in the artificially aged (T6) condition exhibited a coating morphology similar to AA6060-T6, while CCC formation on homogenised AlMg0.5Si0.4 was characterised by growth of localised oxide particles and filaments, resulting in poor coverage. These observations indicated that precipitation of Mg₂Si particles due to heat treatment promoted nucleation of the CCC. Chromate treatment caused a significant reduction of cathodic activity on AA6060 during subsequent polarisation in chloride solution. This was attributed to rapid formation of a thin chromium oxide film on the α-Al(Fe,Mn)Si particles during the chromate treatment, resulting in significant cathodic passivation of the phase. Inhibition of the oxygen reduction reaction at cathodic intermetallic particles is suggested as an important factor contributing to the high performance of chromate pre-treatments on aluminium.